Interface Engineering for High-Performance Top-Gated MoS2 Field-Effect Transistors
(2014-09-24)
Zou, Xuming
;
Wang, Jingli
;
Chiu, Chung-Hua
;
Wu, Yun
;
Xiao, Xiangheng
Experimental evidence of the optimized interface engineering effects in MoS2 transistors is demonstrated. The MoS2/Y2O3/HfO2 stack offers excellent interface control. Results show that HfO2 layer can be scaled down to 9 nm, yet achieving a near-ideal sub-threshold slope (65 mv/dec) and the highest saturation current (526 mu A/mu m) of any MoS2 transistor reported to date.
Low Interface Trap Densities and Enhanced Performance of AlGaN/GaNMOS High-Electron Mobility Transistors Using Thermal Oxidized Y2O3 Interlayer
(2015-12-01)
Liao, Chongnan
;
Zou, Xuming
;
Huang, Chun-Wei
;
Wang, Jingli
;
Zhang, Kai
AlGaN/GaN metal-oxide-semiconductor high-electron mobility transistors (MOS-HEMTs) with Y2O3 interlayer have been investigated to improve the interface quality. With the HfO2/Y2O3 stack gate dielectrics, the devices show a saturated drain current density of up to similar to 943 mA/mm. Meanwhile, the pulsed I-d-V-g measurement indicates interface traps are as low as 5.2 x 10(11) cm(-2), and the pulsed-IV measurement exhibits great resistance to current collapse. Furthermore, the devices also present good reliability under negative bias stress. Therefore, the interface engineering based on Y2O3 has a potential to open up a new avenue to high-performance AlGaN/GaN MOS-HEMTs.