The orientation effect of silicon grains on diamond deposition

Abstract

Diamond deposition on mirror-polished polycrystalline silicon substrates which have grains in various orientations has been investigated using electron backscatter diffraction (EBSD) method with scanning electron microscopy (SEMI). Diamond was deposited by microwave plasma chemical vapor deposition with application of a negative bias voltage oil the substrate. The evidence from systematic SEM observations shows that silicon orientation determined by EBSD has a strong effect on diamond nucleation. In general, the diamond nucleation density on Si grains oriented close to < 100 > is the highest, while it is the lowest for those grains close to < 111 >, under the same experimental conditions for deposition. The same phenomena have been observed in the range of methane concentration from 2% to 4% in hydrogen. (c) 2005 Elsevier B.V. All rights reserved.