標題: Fabrication and Characterization of Mg-Doped ZnO Nanorod Arrays
作者: Liao, Hung-Chou
Chen, San-Yuan
Peng, Cheng-Hsiung
Lin, Chin-Ching
Cheng, Syh-Yuh
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: ZnO Nanorods;Annealing;Doped
公開日期: 1-七月-2010
摘要: Photoelectronic characteristics are investigated in well-aligned MgO-coated ZnO nanorods (MgO/ZnO nanocables) grown on Si substrates buffered with ZnO film at a low temperature by solution techniques. Transmission electron microscopy shows that a rough surface was observed for the MgO-coated ZnO nanorods due to deposition of MgO nanoparticles on the surface of the ZnO nanorods. However, after annealed at high temperatures, the surface of the MgO-coated ZnO nanorods was flattened to form Mg-doped ZnO nanorods. Photoluminescence spectra of Mg-doped ZnO nanorods displayed a blue shift of the near-band-edge emission with increasing annealing temperature indicative of an increase in the band gap of the MgZnO alloy due to diffusion of the Mg atoms into the ZnO nanorods. In contrast, no blue shift was detected for the samples annealed in H(2)/N(2) (5%/95%) reduction atmosphere but a blue emission was detected at 800 degrees C, indicating that MgO diffusion process may produce a new luminescent center to emit the blue emission in H(2)/N(2) reduction atmosphere.
URI: http://dx.doi.org/10.1166/jnn.2010.1693
http://hdl.handle.net/11536/8901
ISSN: 1533-4880
DOI: 10.1166/jnn.2010.1693
期刊: JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY
Volume: 10
Issue: 7
起始頁: 4696
結束頁: 4700
顯示於類別:會議論文