    A gold-free fully copper-metallized InP heterojunction bipolar transistor using non-alloyed ohmic contact and platinum diffusion barrier
    (2005)
    Chang, SW
    ;
    Chang, EY
    ;
    Lee, CS
    ;
    Chen, KS
    ;
    Tseng, CW
    A gold-free, fully Cu-metallized InP heterojunction bipolar transistor using non-alloyed Ti/Pt/Cu and Pt/Ti/Pt/Cu ohmic contacts and platinum diffusion barrier has been successfully fabricated. The InGaAs/Ti/Pt/Cu ohmic structure was stable after annealing up to 350 degrees C as judged from the Auger depth profiles. A current-accelerated stress test was conducted on the device with a current density J(C) = 80kA/cm(2) for 24h, and the current gain showed no degradation after the current stress. The devices were also thermally annealed at 200 degrees C for 3 h and showed almost no change in the electrical parameters after the heat treatment. The results show that the Au-free, fully Cu-metallized InP heterojunction bipolar transistor (HBT) can be realized using non-alloyed ohmic contacts and Pt diffusion barrier.
  • Thumbnail Image
    Item type:Item,
    Gold-free fully cu-metallized InGaP/GaAs heterojunction bipolar transistor
    (2005-01-01)
    Chang, SW
    ;
    Chang, EY
    ;
    Biswas, D
    ;
    Lee, CS
    ;
    Chen, KS
    A gold-free, fully Cu-metallized InGaP/GaAs heterejunction bipolar transistor using platinum as the diffusion barrier has been successfully fabricated. The HBT uses Pd/Ge and Pt/Ti/Pt/Cu for n-type and p(+)-type ohmic contacts, respectively, and Ti/Pt/Cu for interconnect metals with platinum as the diffusion barrier. The Ti/Pt/Cu structure was stable during annealing up to 350degreesC judging from the X-ray diffraction (XRD) data and sheet resistance. A current-accelerated stress test was conducted on the device with a current density J(C) = 140 kA/cm(2) for 24 h, and the current gain showed no degradation. The devices were also thermally annealed at 250degreesC,for 24 h and showed little change. We have successfully demonstrated that an Au-free, fully Cu-metallized HBT can be realized using Pt as the diffusion barrier and Pd/Ge and Pt/Ti/Pt/Cu as the ohmic contacts.