    Broadband Omnidirectional Light Trapping in Gold-Decorated ZnO Nanopillar Arrays
    (2017-04-05)
    Chang, Yuan-Ming
    ;
    Lin, Man-Ling
    ;
    Lai, Tung-Yen
    ;
    Chen, Chang-Hung
    ;
    Lee, Hsin-Yi
    The photoluminescence (PL) and reflectivity characteristics of zinc oxide nanopillars- (ZnO-NPs) grown on indium tin oxide (ITO)-coated glasses were investigated. The room temperature PL showed bright -white -light emission for the undoped ZnO-NPs grown at 600 degrees C, suggesting the close relation between the optical characteristic and "the growth conditions being, carried out for,obtaining the present ZnO-NPs. The reflectivity of the as -grown ZnO-NPs array was about, similar to 29% with the wavelength of the incident light ranging from 200 to 1800 nm. Nevertheless, the reflectance reduced significantly to less than 9.9% when a layer of gold (Au) was deposited on ZnO=NPg by sputtering for 5 min, corresponding to more than 65% reduction in Au -coated ZnQ-NPs (Au/ZnO-NPs). Moreover, the angle -resolved reflectance measurement's on the present Au/ZnO-NPs array show an omnidirectional light -trapping characteristic. These remarkable characteristics, broadband and omnidirectional light -trapping -of Ati/ZnO-NPs, are attributed to the extended effective optical path of the incident light due to subwavelength scattering resulting,from the presence of Au nanoparticics.
  • Thumbnail Image
    Item type:Item,
    Optoelectronic properties in vertically aligned ZnO/Si-nanopillars
    (2012)
    Lee, Hsin-Yi
    ;
    Chang, Yuan-Ming
    ;
    Tseng, Wen-Shou
    ;
    Kao, Pin-Hsu
    ;
    Wang, Hau-Wei
    An effective method of fabricating vertically aligned silicon nanopillars (Si-NPs) was realized by using the self-assembled silver nanodots as natural metal-nanomask for subsequent etching process. Ultrathin (similar to 9 nm) ZnO films were deposited on the Si-NPs by atomic layer deposition to enhance the field emission property. The turn-on field defined by the 10 mu A/cm(2) current density criterion is similar to 0.74 V/mu m with an estimated beta similar to 1.33X10(4). The low turn-on field and marked enhancement in beta were attributed to the small radius of curvature, high aspect ratio, and perhaps more importantly, proper density distribution of the ZnO/Si-NPs. On the other hand, room-temperature ultraviolet (UV) luminescence was investigated for the atomic layer deposited ZnO films grown on Si nanowires fabricated by self-masking dry etching in hydrogen-containing plasma. For films deposited at 200 degrees C, an intensive UV emission corresponding to free-exciton recombination was observed with a nearly complete suppression of the defect-associated broad visible range emission peak.
  • Thumbnail Image
    Item type:Item,
    Field Emission in Vertically Aligned ZnO/Si-Nanopillars with Ultra Low Turn-On Field
    (2012-03-01)
    Chang, Yuan-Ming
    ;
    Liu, Mao-Chen
    ;
    Kao, Pin-Hsu
    ;
    Lin, Chih-Ming
    ;
    Lee, Hsin-Yi
    An effective method of fabricating vertically aligned silicon nanopillars (Si-NPs) was realized by using the self-assembled silver (Ag) nanodots as natural metal-nanomask during dry etching process. The obtained Si-NPs were preferentially aligned along the c-axis direction. Ultrathin ZnO films (similar to 9 nm) were subsequently deposited on the Si-NPs by atomic layer deposition (ALD) to enhance the field emission property. The average diameter of the ZnO/Si-NPs is in the order of tens of nanometers, which enables efficient field emission and gives rise to marked improvement in the field enhancement factor, beta. The turn-on field defined by the 10 mu A/cm(2) current density criterion is similar to 0.74 V/mu m with an estimated beta approximate to 1.33x10(4). The low turn-on field and marked enhancement in beta were attributed to the small radius of curvature, high aspect ratio, and perhaps more importantly, proper density distribution of the ZnO/Si-NPs.
  • Thumbnail Image
    Item type:Item,
    Enhanced Free Exciton and Direct Band-Edge Emissions at Room Temperature in Ultrathin ZnO Films Grown on Si Nanopillars by Atomic Layer Deposition
    (2011-11-01)
    Chang, Yuan-Ming
    ;
    Shieh, Jiann
    ;
    Chu, Pei-Yuan
    ;
    Lee, Hsin-Yi
    ;
    Lin, Chih-Ming
    Room-temperature ultraviolet (UV) luminescence was investigated for the atomic layer deposited ZnO films grown on silicon nanopillars (Si-NPs) fabricated by self-masking dry etching in hydrogen-containing plasma. For films deposited at 200 degrees C, an intensive UV emission corresponding to free-exciton recombination (similar to 3.31 eV) was observed with a nearly complete suppression of the defect-associated broad visible range emission peak. On the other hand, for ZnO films grown at 25 degrees C, albeit the appearance of the defect-associated visible emission, the UV emission peak was observed to shift by similar to 60 meV to near the direct band edge (3.37 eV) recombination emission. The high-resolution transmission electron microscopy (HRTEM) showed that the ZnO films obtained at 25 degrees C were consisting of ZnO nanocrystals with a mean radius of 2 nm embedded in a largely amorphous matrix. Because the Bohr radius of free-exictons in bulk ZnO is similar to 2.3 nm, the size confinement effect may have occurred and resulted in the observed direct band edge electron-hole recombination. Additionally, the results also demonstrate order of magnitude enhancement in emission efficiency for the ZnO/Si-NP structure, as compared to that of ZnO directly deposited on Si substrate under the same conditions.