    Formation of self-assembled ZnTe quantum dots on ZnSe buffer layer grown on GaAs substrate by molecular beam epitaxy
    (2002-07-01)
    Kuo, MC
    ;
    Yang, CS
    ;
    Tseng, PY
    ;
    Lee, J
    ;
    Shen, JL
    Self-assembled ZnTe quantum dot structures were grown by molecular beam epitaxy on GaAs substrates with a 200 nm ZnSe buffer layer. Surface morphology was studied by atomic force microscopy. A three-dimensional Volmer-Weber growth mode was identified. Two types of dots were observed. Strong photoluminescence observed at 1.9-2.2 eV was attributed to emission from the large type II ZnTe quantum dots. Emission from the smaller ZnTe quantum dots was observed at an energy of around 2.26 eV. The density of the larger and smaller dots was approximately 10(8)/cm(2) and 10(9)/cm(2), respectively. (C) 2002 Elsevier Science B.V. All rights reserved.
  • Thumbnail Image
    Item type:Item,
    Growth mode transfer of self-assembled CdSe quantum dots grown by molecular beam epitaxy
    (2006-01-15)
    Lai, YJ
    ;
    Lin, YC
    ;
    Fu, CP
    ;
    Yang, CS
    ;
    Chia, CH
    Self-assembled CdSe/ZnSe quantum dots (QDs) were grown at various growth temperatures on GaAs (0 0 1) by molecular beam epitaxy. An optimum growth temperature for CdSe/ZnSe QDs was found to be 260 degrees C. The Stranski-Krastanow (SK) growth mode was confirmed clearly by atomic force microscopy images. The coherent SK QDs were observed from 2.5 monolayers (MLs). Two types of QDs were found with the CdSe coverage of 3.0 MLs. It was attributed to a growth mode change from the coherent SK growth mode to the ripening growth mode. A schematic diagram of the growth mechanism of self-assembled CdSe QDs was presented. Moreover, the photoluminescence spectra of samples with various thicknesses were investigated. A dramatic change of optical properties confirmed that the QD structure formed with thickness above 2.5 MLs. Finally, the dot size and the density distributions were controlled after growth by in-chamber thermal annealing. For the sample grown at 3.0 MLs, the distribution of dot sizes was controlled from 6.0 to 6.5 x 10(3) nm(3) at an annealing temperature of 400 degrees C. (c) 2005 Published by Elsevier B.V.