Title: | Enhancement of the optical and electrical properties in InGaAlP/InGaP PIN heterostructures by rapid thermal annealing on misoriented substrate |
Authors: | Chin, A Lin, HY Lin, BC 交大名義發表 電子工程學系及電子研究所 National Chiao Tung University Department of Electronics Engineering and Institute of Electronics |
Issue Date: | 1-Jul-1996 |
Abstract: | We have studied the optical and electrical properties of InGaAlP/InGaP PIN heterostructures by the effects of post-growth annealing, substrate misorientation and growth temperature. For the as-grown p-type In-0.5(Ga0.5Al0.5)(0.5)P, the 15 degrees misoriented sample shows the largest hole concentration of 1 x 10(18) cm(-3) as compared to 20 and 10 degrees misoriented samples. After annealing at 900 degrees C for 30 s, the hole concentration increases about three times to 2.6 x 10(18) cm(-3). The increased hole concentration is related to the four times enhanced photoluminescence (PL) intensity. In the In0.6Ga0.4P/In-0.5(Ga0.6Al0.4)(0.5)P stained multiple quantum wells, the post-growth annealing also improves the PL integrated intensity. The PL intensity on an as-grown sample decreases with the increased degree of misorientation, while the PL peak energy increases with the increased degree of misorientation, from 0 degrees, 2 degrees, 10 degrees toward 15 degrees. The PL intensities are larger for samples grown at 760 degrees C than those grown at 700 degrees C. Copyright (C) 1996 Elsevier Science Ltd. |
URI: | http://dx.doi.org/10.1016/0038-1101(95)00415-7 http://hdl.handle.net/11536/1187 |
ISSN: | 0038-1101 |
DOI: | 10.1016/0038-1101(95)00415-7 |
Journal: | SOLID-STATE ELECTRONICS |
Volume: | 39 |
Issue: | 7 |
Begin Page: | 1005 |
End Page: | 1009 |
Appears in Collections: | Articles |
Files in This Item:
If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.