標題: Growth and physical characterization of polygon prismatic hollow Zn-ZnO crystals
作者: Liu, KH
Lin, CC
Chen, SY
材料科學與工程學系
Department of Materials Science and Engineering
公開日期: 1-Mar-2005
摘要: A hierarchical polygon prismatic Zn-ZnO core-shell structure was grown on silicon by combining liquid-solution colloidals together with the vapor-gas growth process. Zn colloidals with a diameter of 5-10 nm synthesized from Zn(ClO4)(2) precursor solution were used as nucleation seeds for the growth of Zn polygon prismatic nanocrystals. Depending on carrier gas and annealing conditions, the polygon prismatic Zn crystals having morphology from hollow to dense configuration can be manipulated. Moreover, after prolonged thermal treatment at 300-400 degrees C, polygon prismatic hollow ZnO-Zn crystals with a dimension from nanometer to micrometer can be obtained. The room-temperature photoluminescence spectra show that the hollow ZnO-Zn crystals have a weak ultraviolet (UV) emission at 380 nm and a strong green emission at 500 nm. However, the intensity of the UV emission can be improved by postannealing the Zn-ZnO core-shell structure in an oxygen atmosphere to form hollow ZnO crystals.
URI: http://dx.doi.org/10.1021/cg0498150
http://hdl.handle.net/11536/13931
ISSN: 1528-7483
DOI: 10.1021/cg0498150
期刊: CRYSTAL GROWTH & DESIGN
Volume: 5
Issue: 2
起始頁: 483
結束頁: 487
Appears in Collections:Articles


Files in This Item:

  1. 000227414900016.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.