A Single-Phased Emission-Tunable Phosphor Ca9Y(PO4)(7):Eu2+,Mn2+ with Efficient Energy Transfer for White-Light-Emitting Diodes

Abstract

A series of single-composition emission-tunable Ca9Y(PO4)(7):Eu2+,Mn2+ phosphors were synthesized by solid-state reaction. The energy transfer from Eu2+ to Mn2+ in Ca9Y(PO4)(7) host matrix was studied and demonstrated to be a resonant type via a dipole-quadrupole mechanism with the critical distance of similar to 11 angstrom. The wavelength-tunable white light can be realized by coupling the emission bands centered at 486 and 638 nm ascribed to the contribution From Eu2+ and Mn2+, respectively. By properly tuning the relative composition of Eu2+/Mn2+, chromaticity coordinates of (0.31, 0.33) can be achieved under excitation at 250-440 nm. Moreover, white-light-emitting diodes were fabricated through the integration of 365 nm chips and single composition white-light-emitting phosphors (Ca0.975Eu0.01Mn0.015)(9)Y(PO4)(7) into a single package shows a cool white light of 7200 K, color rendering index of 76, and color coordinates of (0.30, 0.31) close to that of ideal white light can be achieved.