標題: Experimental and theoretical analysis of loading characteristics of different electret media with various properties toward the design of ideal depth filtration for nanoparticles and fine particles
作者: Tien, Chi-Yu
Chen, Jiang-Ping
Li, Shihang
Li, Ziyi
Zheng, Yu-Ming
Peng, Andy S.
Zhou, Fubao
Tsai, Chuen-Jinn
Chen, Sheng-Chieh
環境工程研究所
Institute of Environmental Engineering
關鍵字: Indoor air quality;Energy-efficient filtration;Ideal depth filtration;Electret composite filter;Holding capacity
公開日期: 15-二月-2020
摘要: Loading experiments of four electret fibrous media having various properties, including fiber diameter, porosity, thickness, charging density and fibrous structure, with fine and nanosized particles were conducted for finding out the influencing factors on efficiency decline and particle holding capacity. The four media include a commercial HVAC media rated with the minimum efficiency reporting value of 13 (MERV13), and three home-made media, including a coarse fiber (CF) layer, a melt-blown (MB) layer, and a bead-on-string (BS) layer. A theoretical model for predicting the pressure drop growth along the loading was applied and compared with that of experiments. The experimental results revealed that the charges of electret media did enhance the holding capacity. The decline of efficiency was found to closely relate to the holding capacity of each media. Higher capacity resulted in a higher decline of efficiency. The theoretical calculation illustrated that the ideal holding capacity was significantly higher than the current electret media had achieved, which indicates that it leaves much improvement of media design more desirable. Comparing the theoretical and experimental results of pressure drop growth with respect to mass load, it was found the current electret layers performed different levels of ideal depth filtration, with an order of CF > MERV13 > BS > MB. Beyond the ideal filtration, pressure drop growth raised exponentially. By utilizing their individual ideal filtration stage, three composite media consisting of 3-4 layers of these electrets with a total thickness less than 1 mm were combined and tested. At 1 in-H2O of pressure drop, the composite electret CF + MERV13 + BS achieved the highest holding capacity with 14.1 g m(-2) which was at least 5-10 times higher than the existing commercial HEPA filters. The bead-onstring fibrous structure of BS enhanced the holding capacity of the composite media significantly. The newly developed electret-based composite filters performed an energy efficient filtration for fine and nanosized particles.
URI: http://dx.doi.org/10.1016/j.seppur.2019.116002
http://hdl.handle.net/11536/153013
ISSN: 1383-5866
DOI: 10.1016/j.seppur.2019.116002
期刊: SEPARATION AND PURIFICATION TECHNOLOGY