標題: Matched glass-to-Kovar seals in N-2 and Ar atmospheres
作者: Kuo, Cheng-hsien
Cheng, Pi-ying
Chou, Chang-pin
機械工程學系
Department of Mechanical Engineering
關鍵字: Kovar alloy;glass;sealing;argon;nitrogen;oxidation;wetting
公開日期: 1-九月-2013
摘要: The oxidation of Kovar alloy was investigated, the wetting and spreading behavior of hard and soft glasses on Kovar alloy were studed by using the sessile drop method, and the quality and the seal strength of glass-Kovar seals were tested. The experimental results indicated that the preoxidation of Kovar alloy for approximately 10 min at 700A degrees C in air resulted in excellent adherence in glass-Kovar seals. The wetting and spreading behavior of glass on preoxidized Kovar alloy were superior to that on nonoxidized Kovar alloy. The wetting ability of ASF110 glass, at 950A degrees C and 980A degrees C in Ar and N-2 atmospheres, was significantly superior to that of ASF200R and ASF700 glasses. The seal quality of the glass-preoxidized Kovar seal was superior to that of the glass-nonoxidized Kovar seal. The shear strength of the ASF110 glass-preoxidized Kovar seal, which was prepared at 980A degrees C for 20 min in an Ar atmosphere, was approximately 3.9 MPa.
URI: http://dx.doi.org/10.1007/s12613-013-0809-1
http://hdl.handle.net/11536/22787
ISSN: 1674-4799
DOI: 10.1007/s12613-013-0809-1
期刊: INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS
Volume: 20
Issue: 9
起始頁: 874
結束頁: 882
顯示於類別:期刊論文


文件中的檔案:

  1. 000324097300009.pdf

若為 zip 檔案,請下載檔案解壓縮後,用瀏覽器開啟資料夾中的 index.html 瀏覽全文。