標題: Oxygen annealing effect on field-emission characteristics of hydrothermally synthesized Al-doped ZnO nanowires
作者: Wang, Jyh-Liang
Hsieh, Tsang-Yen
Yang, Po-Yu
Hwang, Chuan-Chou
Shye, Der-Chi
Lee, I-Che
電子工程學系及電子研究所
Department of Electronics Engineering and Institute of Electronics
關鍵字: Al-doped zinc oxide (AZO);Hydrothermal growth;Nanowire;Field emission;Oxygen annealing
公開日期: 1-九月-2013
摘要: Al-doped ZnO (AZO) nanowires (NWs) were synthesized using low-temperature hydrothermal growth to investigate field emission (FE) characteristics. The intensity ratio of NBE peak to DLE peak (R = I-NBE/I-DLE) increases and the half-maximum of NBE peaks (FWHMNBE) decreases with the Al contents. Experimental results reveal the FE characteristics of AZO NWs are functions of Al content. Moreover, the larger R value and the smaller FWHMNBE are found as the oxygen annealing temperature increases. The hydrothermal AZO NWs annealed in oxygen ambience with an appropriate temperature (i.e. 300-500 degrees C) can demonstrate the further improved FE properties (i.e. the turn-on field of 1.70 V/mu m (at 1 mu A/cm(2)), threshold field of 2.92 V/mu m (at 1 mA/cm(2)), and beta of 4547). (C) 2012 Elsevier B.V. All rights reserved.
URI: http://dx.doi.org/10.1016/j.surfcoat.2012.01.019
http://hdl.handle.net/11536/23330
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2012.01.019
期刊: SURFACE & COATINGS TECHNOLOGY
Volume: 231
Issue: 
起始頁: 423
結束頁: 427
顯示於類別:期刊論文


文件中的檔案:

  1. 000328094200089.pdf

若為 zip 檔案,請下載檔案解壓縮後,用瀏覽器開啟資料夾中的 index.html 瀏覽全文。