標題: High-yield water-based synthesis of truncated silver nanocubes
作者: Chang, Yun-Min
Lu, I-Te
Chen, Chih-Yuan
Hsieh, Yu-Chi
Wu, Pu-Wei
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: Silver nanoparticles;Truncated nanocubes;Hydrothermal synthesis;CTAB;Glucose reduction
公開日期: 15-二月-2014
摘要: A high-yield water-based hydrothermal synthesis was developed using silver nitrate, ammonia, glucose, and cetyltrimethylammonium bromide (CTAB) as precursors to synthesize truncated silver nanocubes with uniform sizes and in large quantities. With a fixed CTAB concentration, truncated silver nanocubes with sizes of 49.3 +/- 4.1 nm were produced when the molar ratio of glucose/silver cation was maintained at 0.1. The sample exhibited (100), (110), and (111) planes on the facets, edges, and corners, respectively. In contrast, with a slightly larger glucose/silver cation ratio of 0.35, well-defined nanocubes with sizes of 70.9 +/- 3.8 nm sizes were observed with the (100) plane on six facets. When the ratio was further increased to 1.5, excess reduction of silver cations facilitated the simultaneous formation of nanoparticles with cubic, spherical, and irregular shapes. Consistent results were obtained from transmission electron microscopy, scanning electron microscopy, X-ray diffraction, and UV-visible absorption measurements. (C) 2013 Elsevier B. V. All rights reserved.
URI: http://dx.doi.org/10.1016/j.jallcom.2013.10.047
http://hdl.handle.net/11536/23577
ISSN: 0925-8388
DOI: 10.1016/j.jallcom.2013.10.047
期刊: JOURNAL OF ALLOYS AND COMPOUNDS
Volume: 586
Issue: 
起始頁: 507
結束頁: 511
顯示於類別:期刊論文