dc.description.abstractFilms of Pbx/100La(x)/100(Zry/100 Tiz/100)1-x/400O3 with x = 8, y = 65 and z = 35 (PLZT(8/65/35)) with a single perovskite structural phase were successfully prepared by using drying-control chemical additives in sol-gel processing followed by rapid thermal annealing at 600-degrees-C for only 1 min on Si(Pt) substrates. The roles of the drying-control chemical additives ethylene glycol and formamide in the gel preparation were studied. The hysteresis loop of PLZT(8/65/35) thin film was measured. The remanent polarization and coercive field were found to be about 1.3 muC cm-2 and 15 kV cm-1, respectively.en_US
dc.language.isoen_USen_US
dc.titleTHE ROLE OF DRYING-CONTROL CHEMICAL ADDITIVES ON THE PREPARATION OF SOL-GEL DERIVED PLZT THIN-FILMSen_US
dc.typeArticleen_US
dc.identifier.doi10.1007/BF00356416en_US
dc.identifier.journalJOURNAL OF MATERIALS SCIENCEen_US
dc.citation.volume28en_US
dc.citation.issue24en_US
dc.citation.spage6691en_US
dc.citation.epage6698en_US
dc.contributor.department工學院zh_TW
dc.contributor.departmentCollege of Engineeringen_US
dc.identifier.wosnumberWOS:A1993MN41500028-
dc.citation.woscount20-
Appears in Collections:Articles