CO[POLY(ETHYLENE TEREPHTHALATE-P-OXYBENZOATE)] THERMOTROPIC COPOLYESTER .2. X-RAY-DIFFRACTION ANALYSIS

Abstract

A series of co [poly (ethylene terephthalate-p-oxybenzoate)] thermotropic copolyester with different compositions were prepared by the copolymerization of either poly(ethylene terephthalate) (PET) polymer or its oligomer with p-acetoxy-benzoic acid. The polymeric products were subjected to solid-state polymerization for various time intervals. Effects of composition ratio and solid-state polymerization time on X-ray diffraction behavior were investigated. It is found that the effect of transesterification induced by solid-state polymerization causes an increase in crystallinity with the copolyesters having high mol % of p-oxybenzoic acid (POB) moiety and causes a decrease in crystallinity with the copolyesters having high mol % of PET moiety. In general, the crystallinity of copolyesters is first increased and then decreased as solid-state polymerization time proceeds. However, the crystallinity of copolyester having POB/PET = 80/20 composition is increased generally at 4-h solid-state polymerization. It is also found that the crystallinity of copolyesters is decreased by quenching. The copolyester based upon either PET oligomer with 4-h solid-state polymerization or PET polymer with 8-h solid-state polymerization shows the most similar X-ray diffraction pattern with that of Eastman 10109.