dc.description.abstractThe phase transformation in Zn-4 Al-3 Cu alloy employing various solution-treatment temperatures (230 degrees C to 325 degrees C) was studied by means of microhardness, scanning electron microscopy (SEM), electron probe microanalysis (EPMA), transmission electron microscopy (TEM), and X-ray diffraction (XRD). The starting microstructure of the as-cast Zn-4Al-3Cu alloy consists of an alpha phase (aluminum-rich, fee structure) in the eta matrix (zinc-rich, h.c.p. structure) prior to solution-treatment. A platelike epsilon phase with 3-mu m length and 0.5-mu m thickness was found in the eta phase matrix after solution-treating the as-cast material at 240 degrees C for 1 hour. The epsilon phase was then dissolved gradually back into the eta matrix above that temperature. A four-phase transformation, alpha + epsilon --> T' + eta, was observed from the temperature 250 degrees C to 310 degrees C, wherein the T' phase formed at the interface of epsilon platelet and eta phase matrix. This T' phase was further identified as a rhombohedral structure. As the solution-treatment temperature was increased to above 310 degrees C, the epsilon phase was completely dissolved back into the eta matrix and numerous beta phase particles were distributed uniformly in the eta matrix. The beta phase subsequently decomposed at room temperature to a fine alpha phase embedded in the eta matrix. For the materials solution-treated above 250 degrees C, the microhardness of the eta matrix increased in 40 minutes during natural aging, which was associated with the formation of fine epsilon phase of 0.15 mu m diameter. The orientation relationship between this fine epsilon phase and eta phase was determined as [(1) over bar 011](eta) // [(1) over bar 011](epsilon), (01 (1) over bar 2)(eta) // (01 (1) over bar 2)(epsilon).en_US
dc.language.isoen_USen_US
dc.titlePhase transformation of Zn-4Al-3Cu alloy during heat treatmenten_US
dc.typeArticleen_US
dc.identifier.journalMETALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCEen_US
dc.citation.volume30en_US
dc.citation.issue4en_US
dc.citation.spage917en_US
dc.citation.epage923en_US
dc.contributor.department材料科學與工程學系zh_TW
dc.contributor.departmentDepartment of Materials Science and Engineeringen_US
dc.identifier.wosnumberWOS:000079411000003-
dc.citation.woscount8-
顯示於類別:期刊論文


文件中的檔案:

  1. 000079411000003.pdf

若為 zip 檔案,請下載檔案解壓縮後,用瀏覽器開啟資料夾中的 index.html 瀏覽全文。