标题: Effects of Rhenium on Microstructure and Phase Stability of MAR-M247 Ni-Base Fine-Grain Superalloy
作者: Liao, Jian-Hong
Bor, Hui-Yun
Chao, Chuen-Guang
Liu, Tzeng-Feng
材料科學與工程學系
Department of Materials Science and Engineering
关键字: superalloy;rhenium;fine-grain;casting
公开日期: 1-四月-2010
摘要: The effects of Re additions on the microstructure and phase stability of the cast fine-grain Mar-M247 superalloy were investigated in this study. The results showed that the grain sizes of the alloys with 0, 3, and 4.5 mass% Re content were 90, 60, and 50 mu m, respectively. The primary gamma' phase became finer and more cuboidal as Re content increased. The addition of 3 mass% Re caused strip-like MC carbides within the grain to degenerate into discontinuous M(23)C(6) carbides and initiated the formation of a deleterious topological closed-packed (TCP) phase within the grain interior. The addition of 4.5 mass% Re promoted phase instabilities that led to the precipitation of large amounts of needle-like P phase in the grain interior, attributable to Re and W segregation. This study found that 3 mass% Re was a critical addition to maintain optimal microstructure and phase stability, and improved the ultimate tensile strength and the yield strength at room temperature and 760 degrees C. However, the addition of 4.5 mass% Re obviously resulted in a decrease in tensile properties at room temperature and 760 degrees C. [doi:10.2320/matertrans.M2009331]
URI: http://dx.doi.org/10.2320/matertrans.M2009331
http://hdl.handle.net/11536/5552
ISSN: 1345-9678
DOI: 10.2320/matertrans.M2009331
期刊: MATERIALS TRANSACTIONS
Volume: 51
Issue: 4
起始页: 810
结束页: 817
显示于类别:Articles


文件中的档案:

  1. 000278263100035.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.