dc.description.abstract本研究針對La4Ti9O24陶瓷，添加TEOS ( Tetraethoxysilane )包覆之高氧化鉛含量玻璃粉進行水系刮刀成型薄片研究以應用於高介電微波陶瓷元件。藉由TEOS水解聚縮合反應對高含鉛量玻璃粉進行表面包覆改質已獲致良好的效果，應用於水系漿料中進行低溫液相燒結於1000 ℃燒結4小時後有明顯的La0.66TiO2.993陶瓷相產生。並成功以自行組裝之動態燒結收縮率測量裝置量測添加TEOS包覆玻璃粉La4Ti9O24生胚薄片X-Y軸向的動態燒結收縮率變化。zh_TW
dc.description.abstractAn aqueous-based slip for tape-casting of La4Ti9O24 ceramic sheets with TEOS ( Tetraethoxysilane ) coated high lead oxide contained glass was studied that is suitable for application of high dielectric constant microwave devices. High lead oxide contained glass powder was modified by TEOS hydrolysis-polycondensation coating process; by adding this modified glass powder with La4Ti9O24 ceramic powder sintered 4 hours at 1000 ℃ was obtained La0.66TiO2.993 ceramic phase. The tape shrinkage ratio in X-Y axes was successfully measured by using assembled dynamic-shrinkage-behavior Laser Scan Micrometer.en_US
dc.language.isozh_TWen_US
dc.subjectLa4Ti9O24陶瓷zh_TW
dc.subjectTEOS ( Tetraethoxysilane )zh_TW
dc.subject水系刮刀成型zh_TW
dc.subject微波陶瓷元件zh_TW
dc.subject低溫液相燒結zh_TW
dc.subjectLa0.66TiO2.993陶瓷zh_TW
dc.subject動態燒結收縮率測量裝置zh_TW
dc.subjecttape-castingen_US
dc.subjectLa4Ti9O24 ceramicen_US
dc.subjectTetraethoxysilaneen_US
dc.subjectmicrowave devicesen_US
dc.subjecthydrolysis-polycondensationen_US
dc.subjectLa0.66TiO2.993 ceramicen_US
dc.subjectdynamic-shrinkage-behavior Laser Scan Micrometeren_US
dc.titleLa4Ti9O24陶瓷添加TEOS包覆玻璃粉之水系刮刀成型薄片研究zh_TW
dc.titleAqueous Tape Casting of La4Ti9O24 Ceramic System with TEOS Coated Glassen_US