標題: Synthesis and characterization of quaternary chalcogenides InSn(2)Bi(3)Se(8) and In(0.2)Sn(6)Bi(1.8)Se(9)
作者: Wang, Ming-Fang
Jang, Shyue-Ming
Huang, Jih-Chen
Lee, Chi-Shen
應用化學系
Department of Applied Chemistry
公開日期: 1-Jun-2009
摘要: Quaternary chalcogenides InSn(2)Bi(3)Se(8) and In(0.2)Sn(6)Bi(1.8)Se(9) were synthesized on direct combination of their elements in stoichiometric ratios at T>800 degrees C under vacuum. Their structures were determined with X-ray diffraction of single crystals. InSn(2)Bi(3)Se(8) crystallizes in monoclinic space group C2/m (No. 12) with a = 13.557(3) angstrom, b = 4.1299(8) angstrom, c = 15.252(3)angstrom, beta = 115.73(3)degrees, V = 769.3(3) angstrom(3), Z = 2, and R(1)/wR(2)/GOF = 0.0206/0.0497/1.092; In(0.2)Sn(6)Bi(1.8)Se(9) crystallizes in orthorhombic space group Cmc2(1) (No. 36) with a = 4.1810(8) angstrom, b = 13.799(3) angstrom, c = 31.953(6) angstrom, V=1843.4(6) angstrom(3), Z = 4, and R(1)/wR(2)/GOF = 0.0966/0.2327/1.12. InSn(2)Bi(3)Se(8) and In(0.2)Sn(6)Bi(1.8)Se(9) are isostructural with CuBi(5)S(8) and Bi(2)Pb(6)S(9) phases, respectively. The structures of InSn(2)Bi(3)Se(8) and In(0.2)Sn(6)Bi(1.8)Se(9) feature a three-dimensional framework containing slabs of NaCl-(311) type with varied thicknesses. Calculations of the electronic structure and measurements of electrical conductivity indicate that these materials are semiconductors with narrow band gaps. Both compounds show n-type semiconducting properties with Seebeck coefficients -270 and -230 mu V/K at 300 K for InSn(2)Bi(3)Se(8) and In(0.2)Sn(6)Bi(1.8)Se(9), respectively. (C) 2009 Elsevier Inc. All rights reserved.
URI: http://dx.doi.org/10.1016/j.jssc.2009.03.013
http://hdl.handle.net/11536/7174
ISSN: 0022-4596
DOI: 10.1016/j.jssc.2009.03.013
期刊: JOURNAL OF SOLID STATE CHEMISTRY
Volume: 182
Issue: 6
起始頁: 1450
結束頁: 1456
Appears in Collections:Articles