標題: | Colloidal dispersion of nano-scale ZnO powders using amphibious and anionic polyelectrolytes |
作者: | Ying, Kuo-Liang Hsieh, Tsung-Eong Hsieh, Yi-Feng 材料科學與工程學系 Department of Materials Science and Engineering |
關鍵字: | ZnO;Nano-scale dispersion;Polyelectrolytes;Nano-ZnO target |
公開日期: | 1-四月-2009 |
摘要: | This article describes the dispersion of aqueous suspensions containing nano-scale ZnO powder by utilizing a hybrid of chemical dispersant and mechanical mixing/grinding process. The chemical dispersants included anionic or amphibious polyelectrolytes, i.e., sodium salt of polymethylacrylic acid (PMAA-Na) or polyacrylamide/(alpha-N, N-dimethyl-N-acryloyloxyethyl) ammonium ethanate (PDAAE). The optimum critical concentrations for each dispersants to achieve the lowest viscosity, smallest final sediment volume and particle size (d(50)) for the nano-ZnO suspensions, 3 wt.% for PMAA-Na and 5 wt.% for PDAAE, were identified. The finely dispersed nano-ZnO powders were transferred to prepare sputtering target. The root-mean-square roughness (R(Rms)) of thin films deposited by utilizing such a target was found to be 2.05 nm, which was lower than the RRMS of the film (approximate to 27.57 nm) deposited by using a commercial ZnO target comprised of micro-scale granules. (C) 2008 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
URI: | http://dx.doi.org/10.1016/j.ceramint.2008.05.014 http://hdl.handle.net/11536/7416 |
ISSN: | 0272-8842 |
DOI: | 10.1016/j.ceramint.2008.05.014 |
期刊: | CERAMICS INTERNATIONAL |
Volume: | 35 |
Issue: | 3 |
起始頁: | 1165 |
結束頁: | 1171 |
顯示於類別: | 期刊論文 |