標題: Application of Pd/Ge/Cu alloyed ohmic contact system to n-type GaAs for fully Cu-metallized InGaP/GaAs HBTs
作者: Chen, Ke-Shian
Chang, Edward Yi
Lin, Chia-Ching
Lee, Cheng-Shih
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: Copper;GaAs;HBT;Metallization;Ohmic contact
公開日期: 1-Feb-2009
摘要: Use of the Pd/Ge/Cu multilayers as the emitter and collector ohmic metal for the fully Cu-metallized InGaP/GaAs heterojunction bipolar transistors is studied. The Pd/Ge/Cu ohmic contact exhibited a very low contact resistance of 5.73 x 10(-7) Omega cm(2) at a low annealing temperature (250 degrees C) and the microstructure evolution of Pd/Ge/Cu ohmic contact was investigated using transmission electron microscopy and energy dispersive spectrometer. We also did some comparisons between the Pd/Ge/Cu, Pd/Ge/Ti/Pt/Cu, and the traditional Au/Ge/Ni/Au ohmic contact structures to n-type GaAs. The common emitter I-V curves and Gummel plot of these Cu-metallized HBTs using Pd/Ge/Cu ohmic contact and Cu interconnects showed similar electrical characteristics as those HBTs with conventional Au-metallization. The cutoff frequency (f(T)) of 3 x 20-mu m-emitter-area devices was about 38 GHz. During both the current-accelerated stress test (110 kA/cm(2) stress for 24 h) and the thermal stability test (annealing at 250 degrees C for 24 h), the fully Cu-metallized HBT with Pd/Ge/Cu ohmic contact and Cu interconnects showed almost no obvious degradation in electrical characteristics. The results show that the Pd/Ge/Cu ohmic contact in combination with the Cu interconnects can be used on HBT devices to achieve the Au-free fully Cu-metallized lnGaP/GaAs HBTs, and the devices exhibit good device performance. (C) 2008 Elsevier Ltd. All rights reserved.
URI: http://dx.doi.org/10.1016/j.sse.2008.10.017
http://hdl.handle.net/11536/7666
ISSN: 0038-1101
DOI: 10.1016/j.sse.2008.10.017
期刊: SOLID-STATE ELECTRONICS
Volume: 53
Issue: 2
起始頁: 154
結束頁: 159
Appears in Collections:Articles


Files in This Item:

  1. 000263596100009.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.