標題: The effect of hot-dipped aluminum coatings on Fe-8Al-30Mn-0.8C alloy
作者: Su, C. W.
Lee, J. W.
Wang, C. S.
Chao, C. G.
Liu, T. F.
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: Fe-Al-Mn alloy;hot-dip aluminization;corrosion;oxidation;transmission electron microscopy;TEM
公開日期: 1-二月-2008
摘要: The morphology and microstructure of an intermetallic layer formed on the surface of Fe-8Al-30Mn-0.8C alloy by hot-dip aluminization treatment have been examined in detail. The phases present in the coating are unambiguously identified by means of transmission electron microscopy. After alummization, a two layer coating was formed consisting of an external Al layer and a (Fe, Mn)(2)Al-5 intermetallic on top of the substrate. The (Fe,Mn)(2)Al-5 compound has an orthorhombic structure with lattice parameters a = 0.752 nm, b = 0.667 nm and c = 0.417 nm. The activation energy (E-FeMnAl) for the growth of such an intermetallic layer is calculated to be 52.7 kJ/mol. These results are different from those observed in aluminized low-carbon steel (E-Fe). The difference between E-FeMnAl and E-Fe is attributed to the alloying elements (Mn) in the present alloy. Environmental salt fog corrosion and high temperature oxidation tests were carried out to examine the corrosion and oxidation resistance. The results indicated that both the corrosion and oxidation resistance of the Fe-8Al-30Mn-0.8C alloy treated by hot-dip aluminization can be significantly increased. (C) 2007 Elsevier B.V. All rights reserved.
URI: http://dx.doi.org/10.1016/j.surfcoat.2007.08.011
http://hdl.handle.net/11536/9725
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2007.08.011
期刊: SURFACE & COATINGS TECHNOLOGY