標題: Optical characteristics of a-plane InGaN/GaN multiple quantum wells with different well widths
作者: Ko, T. S.
Lu, T. C.
Wang, T. C.
Lo, M. H.
Chen, J. R.
Gao, R. C.
Kuo, H. C.
Wang, S. C.
Shen, J. L.
光電工程學系
Department of Photonics
公開日期: 30-Apr-2007
摘要: a-plane InGaN/GaN multiple quantum wells of different widths ranging from 3 to 12 nm were grown on r-plane sapphire by metal organic chemical vapor deposition for investigation. The peak emission intensity of the photoluminescence (PL) reveals a decreasing trend as the well width increases from 3 to 12 nm. Low temperature (9 K) time-resolved PL study shows that the sample with 3-nm-thick wells has a better optical property with a fast exciton decay time of 0.57 ns. The results of cathodoluminescence and micro-PL scanning images for samples of different well widths further verify the more uniform and stronger luminescence intensity distribution observed for the samples of thinner quantum wells, indicating that the important growth parameters for a-plane InGaN/GaN multiple quantum wells could be dominated by the In fluctuation and crystal quality during the epitaxial growth. (c) 2007 American Institute of Physics.
URI: http://dx.doi.org/10.1063/1.2735935
http://hdl.handle.net/11536/10878
ISSN: 0003-6951
DOI: 10.1063/1.2735935
期刊: APPLIED PHYSICS LETTERS
Volume: 90
Issue: 18
結束頁: 
Appears in Collections:Articles


Files in This Item:

  1. 000246210000022.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.