標題: | STRUCTURES AND PROPERTIES OF THE CRYSTALLINE Si-C-N USING ADDITIONAL Si-SOURCE AND Co-CATALYST |
作者: | Chang, Hui Lin Fang, Jau Shiung Kuo, Cheng Tzu 材料科學與工程學系 Department of Materials Science and Engineering |
公開日期: | 1-十二月-2003 |
摘要: | Si-C-N films were synthesized on Si substrates by microwave plasma chemical vapor deposition (MPCVD) with a mixture of CH4 and N-2 as gaseous sources, and Co-coated Si columns to act as a catalyst and an additional Si source. Two conditions, conditions 1 and 2, were implemented by varying the time at which the solid sources were introduced. Under condition 1, the solid sources were applied \'before\' film deposition. Under condition 2, the solid sources were applied both \'before and during\' film depositions. Analytical results indicate, although that both conditions yield crystalline Si-C-N films, the time at which the solid sources are applied is critically affects the films\' structures and properties. Synthesizing Si-C-N films under condition 1 yields crystals with more re-nucleation, a structure closer to a pseudo T-Si3N4 structure, a higher C content, detectable Si(2p)-C bonding, lower nano-hardness and better field emission properties. Synthesis of film under condition 2 yields, crystals with more facets, a structure closer to pseudo alpha-Si3N4 and an additional thin layer under the crystalline layer. SEM, TEM, XPS, XRD, nanoindentor and field emission were used to characterize the film\' structures and properties. |
URI: | http://hdl.handle.net/11536/124009 |
ISSN: | 1606-5131 |
期刊: | REVIEWS ON ADVANCED MATERIALS SCIENCE |
起始頁: | 432 |
結束頁: | 439 |
顯示於類別: | 期刊論文 |