標題: Size effect on multiferroic TbMn2O5 nanorods
作者: Yang, Chun-Chuen
Tung, Yung-Hsiang
Chen, Yi-Jung
Hsu, Ting-Wei
You, Pang-Yen
Chan, Ting-Shan
Chen, Yang-Yuan
光電工程學系
Department of Photonics
公開日期: 7-May-2015
摘要: The effect of the size of TbMn2O5 on their magnetoelectric properties is studied using a field emission transmission electron microscope, ac magnetic susceptibility, relative dielectric constant, specific heat capacity, and x-ray diffraction at various temperatures. A bulk sample and nanorods with two axial lengths, < L-C >, are investigated. Nanorods with < L-C > of 216 nm and 64 nm crystallize with orthorhombic Pbam symmetry as the bulk material. The axial direction of the two sizes of nanorod is parallel to the c axis of the crystal. No particular radial direction is observed. The critical size for the magnetic ordering of TbMn2O5 is found to be between < L-C > - 64 nm and 216 nm. Experiments on specific heat capacity verified these results. No similar phenomenon concerning the ferroelectric property is observed. At T = 30K and 35 K, the < L-C > - 216 nm sample yields a charge-ordering-like x-ray diffraction peak, which may be associated with the magnetically induced charge ordering superlattice. (C) 2015 AIP Publishing LLC.
URI: http://dx.doi.org/10.1063/1.4913822
http://hdl.handle.net/11536/124819
ISSN: 0021-8979
DOI: 10.1063/1.4913822
期刊: JOURNAL OF APPLIED PHYSICS
Volume: 117
Issue: 17
Appears in Collections:Articles