Photoluminescence and Raman spectroscopy of single diamond nanoparticle

Abstract

The article reports techniques that we have devised for immobilizing and allocating a single nanodiamond on the electron beam (E-beam) lithography patterned semiconductor substrate. By combining the E-beam patterned smart substrate with the high throughput of a confocal microscope, we are able to overcome the limitation of the spatial resolution of optical techniques (similar to 1 mu m) to obtain the data on individual nano-object with a size range between 100 and 35 nm. We have observed a broad photoluminescence centered at about 700 nm from a single nanodiamond which is due to the defects, vacancies in the nanodiamonds, and the disordered carbon layer covered on the nanodiamond surface. We also observe red-shift in energy and broadening in linewidth of the sp(3) bonding Raman peak when the size of the single nanodiamond is reduced due to the phonon-confinement effects.