標題: The Indentation-Induced Pop-in Phenomenon and Fracture Behaviors of GaP(100) Single-Crystal
作者: Chiu, Yi-Jui
Jian, Sheng-Rui
Lee, Jyh-Wei
Juang, Jenh-Yih
電子物理學系
Department of Electrophysics
關鍵字: GaP(100) single crystal;pop-in;nanoindentation;fracture
公開日期: 1-十一月-2019
摘要: The deformation behaviors and fracture features of GaP(100) single-crystal are investigated by using nano- and micro-scale indentation techniques. The hardness and Young's modulus were measured by nanoindentation using a Berkovich diamond indenter with continuous contact stiffness measurements (CSM) mode and the values obtained were 12.5 +/- 1.2 GPa and 152.6 +/- 12.8 GPa, respectively. In addition, the characteristic "pop-in" was observed in the loading portion of load-displacement curve, which was caused by the nucleation and/or propagation of dislocations. An energetic estimation methodology on the associated nanoindentation-induced dislocation numbers resulting from the pop-in events was discussed. Furthermore, the Vickers indentation induced fracture patterns of GaP(100) single-crystal were observed and analyzed using optical microscopy. The obtained fracture toughness K-C of GaP(100) single-crystal was similar to 1.7 +/- 0.1 MPa.m(1/2), which is substantially higher than the K-IC values of 0.8 MPa.m(1/2) and 1.0 MPa.m(1/2) previously reported for of single-crystal and polycrystalline GaP, respectively.
URI: http://dx.doi.org/10.3390/mi10110752
http://hdl.handle.net/11536/153370
DOI: 10.3390/mi10110752
期刊: MICROMACHINES
Volume: 10
Issue: 11
起始頁: 0
結束頁: 0
顯示於類別:期刊論文