Mechanical and tribological properties evaluation of cathodic arc deposited CrN/ZrN multilayer coatings

Abstract

Five nanostructured CrN/ZrN multilayer coatings were deposited periodically by cathodic arc evaporation. The bilayer periods of the CrN/ZrN multilayer coatings were controlled in the range of 5 to 30 nm. The structures and bilayer period of the multilayer coatings were characterized by an X-ray diffractometer. The microstructures of thin films were examined by scanning electron microscopy (SEM) and transmission electron microscopy (TEM), respectively. Nanoindentation, scratch tests, Daimler-Benz Rockwell-C (HRC-DB) adhesion tests, microhardness and pin-on-disk wear tests were used to evaluate the hardness, adhesion, indentation toughness and tribological properties of thin films, respectively. It was found that the hardness and tribological properties were strongly influenced by the bilayer period of the CrN/ZrN multilayer coatings. An optimal combination of mechanical properties and excellent tribological behavior was found for a coating with a critical bilayer period of 30 nm. (C) 2011 Elsevier B.V. All rights reserved.