Transparent Flexible Heteroepitaxy of NiO Coated AZO Nanorods Arrays on Muscovites for Enhanced Energy Storage Application

Abstract

Transparent flexible energy storage devices are considered as important chains in the next-generation, which are able to store and supply energy for electronic devices. Here, aluminum-doped zinc oxide (AZO) nanorods (NRs) and nickel oxide (NiO)-coated AZO NRs on muscovites are fabricated by a radio frequency (RF) magnetron sputtering deposition method. Interestingly, AZO NRs and AZO/NiO NRs are excellent electrodes for energy storage application with high optical transparency, high conductivity, large surface area, stability under compressive and tensile strain down to a bending radius of 5 mm with 1000 bending cycles. The obtained symmetric solid-state supercapacitors based on these electrodes exhibit good performance with a large areal specific capacitance of 3.4 mF cm(-2), long cycle life 1000 times, robust mechanical properties, and high chemical stability. Furthermore, an AZO/NiO//Zn battery based on these electrodes is demonstrated, yielding a discharge capacity of 195 mAh g(-1) at a current rate of 8 A g(-1) and a discharge capacity of over 1000 cycles with coulombic efficiency to 92%. These results deliver a concept of opening a new opportunity for future applications in transparent flexible energy storage.