完整後設資料紀錄
DC 欄位 | 值 | 語言 |
---|---|---|
dc.contributor.author | 黃俊元 | en_US |
dc.contributor.author | Chun-Yuan Huang | en_US |
dc.contributor.author | 陳 衛 國 | en_US |
dc.contributor.author | Wei-Kuo Chen | en_US |
dc.date.accessioned | 2014-12-12T02:20:56Z | - |
dc.date.available | 2014-12-12T02:20:56Z | - |
dc.date.issued | 1998 | en_US |
dc.identifier.uri | http://140.113.39.130/cdrfb3/record/nctu/#NT870429031 | en_US |
dc.identifier.uri | http://hdl.handle.net/11536/64453 | - |
dc.description.abstract | 本論文利用離子佈植的方法,針對氮化鎵薄膜進行矽與磷離子單獨或共同佈植之研究,並藉由快速熱退火處理(Rapid Thermal Anneal, RTA),來瞭解矽、磷離子佈植對氮化鎵薄膜的影響。對於矽離子佈植之氮化鎵,經退火後,其載子濃度隨退火時間有明顯上升,特別於1100℃退火20秒,我們可得最高之矽離子活化率40%,面載子濃度亦高達2x1015 cm-2,此結果可與目前其它研究群之結果相媲美。在矽與磷共同佈植方面,我們發現磷的加入,並無法進一步提升,反而有抑制矽活化率的趨勢,這和傳統砷化鎵或磷化銦材料有著顯著不同。然而,磷的離子佈植卻能有效提升霍爾移動率,改善薄膜的電學品質,其電子移動率數值,甚至可高於未佈植之氮化鎵,由於氮化鎵的磊晶薄膜,通常具有高達108cm-2 的面缺陷濃度,磷如何降低載子運動時的散射碰撞機制,亦是未來氮化鎵研究相當有趣的研究課題。 | zh_TW |
dc.description.abstract | GaN films implanted with 28Si+ and 31P+ were investigated systematically by Hall measurement and photoluminescence method. The activation efficiency of Si behaves quite differently on their implantation conditions. For Si implanted samples, a carrier concentration of 2x1015 cm-2 with ~40% activation efficiency can be obtained after a rapid thermal annealing process at 1100℃, The introduce of P ion during the Si implantation, however, bring an adverse effect on Si activation. The GaN carrier concentration was found to decrease with increase of P/Si ratio and its value is even lower than that of unimplanted ones when high concentration P is co-implanted. Such an outcome is unexpected and is rarely observed in conventional GaAs and InP materials. Nonetheless, we have found that the implantation of P+ alone can improve the Hall mobility dramatically. The reasons accounted for are still not well-understood and more investigations are needed for future study. | en_US |
dc.language.iso | zh_TW | en_US |
dc.subject | 離子佈植 | zh_TW |
dc.subject | 氮化鎵 | zh_TW |
dc.subject | 霍爾量測 | zh_TW |
dc.subject | 矽 | zh_TW |
dc.subject | 磷 | zh_TW |
dc.subject | 摻雜 | zh_TW |
dc.subject | implantation | en_US |
dc.subject | GaN | en_US |
dc.subject | n-type | en_US |
dc.subject | Si | en_US |
dc.subject | P | en_US |
dc.subject | phosphorus | en_US |
dc.subject | TRIM | en_US |
dc.subject | doping | en_US |
dc.title | 氮化鎵離子佈植之特性研究 | zh_TW |
dc.title | Characterizations of Implanted GaN Film | en_US |
dc.type | Thesis | en_US |