標題: | 應用在無線通訊的低雜訊高電子遷移率電晶體之線性度的研究與改善 應用在無線通訊的低雜訊高電子遷移率電晶體之線性度的研究與改善 |
作者: | 林岳欽 Yueh-Chin Lin 張翼 Edward Yi Chang 材料科學與工程學系 |
關鍵字: | 無線通訊;低雜訊;高電子遷移率電晶體;線性度;Wireless Communication;Low Noise;HEMT;Linearity |
公開日期: | 2005 |
摘要: | 這篇論文為研究高電子遷移率電晶體(HEMT)之線性度的改善,此研究首先分析三次交互調變失真(IM3)及三次交叉點(IP3)與轉導值(transconductance)之間的關係,由所推導的結果得知,越平坦的轉導分布圖形之元件的線性度越好,因此本研究分四大部分去探討元件線性度的改善。 首先,我們研究利用複合通道層(composite channel)的變形高電子遷移率電晶體(MHEMT),來發展低雜訊暨高線性度之元件,此研究主要是利用複合通道層能提升電子在通道層的侷限能力進而提升元件之線性度。接著我們研究均勻性摻雜(uniformly doped)與平面性摻雜(planer doped)對元件線性度的影響,本研究驗證均勻性摻雜之變形高電子遷移率電晶體雖然具有較低之最高轉導值,但其轉導值之分布較為平坦,故線性度亦較佳。 對於假形高電子遷移率電晶體(PHEMT),首先我們發展出以砷化鋁鎵(AlGaAs)為spacer的磷化銦鎵/砷化銦鎵(InGaP/InGaAs) 假形高電子遷移率電晶體,由於利用磷化銦鎵為蕭特基層(Schottky layer)可降低元件閘極(Gate)之漏電流及砷化鋁鎵(AlGaAs)為spacer可提升元件之電子遷移率(mobility),因此此元件具有低雜訊及高線性度之特性。 最後我們研究利用額外的電子摻雜,來提升元件的線性度。此研究是以一般平面性摻雜的磷化銦鎵/砷化銦鎵元件為基準,分別額外的摻雜電子在蕭特基層及通道層,探討額外的電子摻雜在不同層時對元件線性度的影響。最後驗證出額外摻雜電子在元件上會使得元件之最大轉導值下降,但其分布會更為平坦,而使得元件之線性度提升。接著提升偏壓條件,對額外摻雜在通道層及蕭特基層做適用是的測試,最後亦驗證得額外摻雜在通道層有較佳的線性度。 In this paper, high-electron-mobility transistors (HEMTs) with doping profile modification are discussed for device linearity improvement. The modification was based on the third-order intermodulation distortion (IM3) and the third-order intercept point (IP3) analysis through simple equivalent circuit of the devices. The correlation of the extrinsic transconductance (Gm) with IM3 and IP3 indicates that flatter Gm distribution vs gate bias voltage causes lower IM3 level and that high Gm with flatter Gm distribution result in higher IP3 of the devices. Therefore, doping modification that improves the flatness of the Gm distribution will improve the device linearity. The study is divided into four parts: First, a metamorphic high-electron-mobility transistor (MHEMT) with In0.55Ga0.45As/In0.67Ga0.33As/In0.55Ga0.45As composite channel layers was developed for low noise and high-linearity applications. The use of a composite channel results in high electron mobility and good confinement of electrons in the channel region which are the desired characteristics of a low-noise and high-linearity device. The device shows great potential for high-linearity and low-noise applications at high frequencies. Second, the uniformly-doped and the δ doped In0.52Al0.48As/In0.6Ga0.4As MHEMT were fabricated and the DC characteristics and the third-order intercept point (IP3) of these devices were measured and compared. Due to more uniform electron distribution in the quantum well region, the uniformly-doped MHEMT exhibits flatter Gm (transconductance) vs IDS ( drain to source current ) curve and much better linearity with higher IP3 and higher IP3 to PDC ratio as compared to the δ doped MHEMT, even though the δ doped device exhibits higher peak transconductance. As a result, the uniformly doped MHEMT is more suitable for communication systems that require high linearity operation. Third, a low noise InGaP/InGaAs pseudomorphic high-electron-mobility transistors (PHEMTs) with high IP3 was developed. The device utilizes InGaP as Schottky layer to achieve a low noise figure and uses AlGaAs as the spacer to improve the electron mobility and the device also uses dual delta doped layers for uniform electron distribution in the channel to improve the device linearity. Finally, doping modification in the Schottky layer (Schottky layer doped) and in the channel layer (channel doped) of the conventional δ doped InGaP/InGaAs PHEMT were experimented to see the extra doping effect on the HEMT device linearity. DC and RF performances of these devices were measured and compared. It is found that extra doping either in the channel region or in the Schottky layer can improve the flatness of the Gm distribution under different gate bias conditions and thus achieve lower IM3 and higher IP3 of these devices with small scarification in the peak Gm value as compared to the conventional delta doped devices. The power performances of these devices were tested with different drain to source voltage (VDS) bias points. When the VDS bias was increased, the Gm values of the channel doped device and the Schottky layer doped device increased and decreased respectively with the increasing VDS bias. The adjacent-channel power ratio (ACPR) measurements of these devices were performed at different DC bias power levels. Overall, it was found that channel doped device demonstrated best linearity performance among these three different types of devices studied with highest IP3 level, lowest IM3 and best ACPR under CDMA modulation even though it has the lowest electron mobility among these devices. Overall, different structures and doping profiles of InGaP/InGaAs PHEMT and InAlGs/InGaAs MHEMT devices were experimented for device linearity improved. It’s found with paper design of the device structure and doping profile, the linearity of the HEMT device can be greatly improved and the experimental results match well with the theoretical analysis in this thesis. |
URI: | http://140.113.39.130/cdrfb3/record/nctu/#GT008918815 http://hdl.handle.net/11536/77890 |
Appears in Collections: | Thesis |
Files in This Item:
If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.