標題: Effect of migration and condensation of pre-existing voids on increase in bump resistance of flip chips on flexible substrates during electromigration
作者: Liang, S. W.
Chang, Y. W.
Chen, Chih
Preciado, Jackie
Tu, K. N.
材料科學與工程學系
Department of Materials Science and Engineering
關鍵字: electromigration;flip-chip solder joints;packaging
公開日期: 1-七月-2008
摘要: In Pb-free solder joints formed by reflowing a bump of solder paste, voids are formed within the solder due to the residue of flux in the reflow process. These voids migrate toward the cathode contact during electromigration under current stressing. Accompanying the electromigration, resistance jumps of a few 100 m Omega were observed. It was postulated that a jump occurs when a void touches the cathode contact. This study investigated the effect of the void migration and condensation on the change in bump resistance using three-dimensional (3D) simulations and finite element analysis. It was found that there was negligible change in bump resistance during void migration towards the high-current-density region before touching the cathode contact opening. When a small void condensed on the contact opening and depleted 18.4% of the area, the bump resistance increased only 0.4 m Omega. Even when a large void depleted 81.6% of the opening, the increase in bump resistance was 3.3 m Omega. These values are approximately two orders of magnitude smaller than those reported in the literature for the change in resistance due to void migration in flip chips on flexible substrates. We conclude that the reported change in resistance was most likely that of the Al or Cu interconnection in the flip-chip samples.
URI: http://dx.doi.org/10.1007/s11664-008-0463-y
http://hdl.handle.net/11536/8626
ISSN: 0361-5235
DOI: 10.1007/s11664-008-0463-y
期刊: JOURNAL OF ELECTRONIC MATERIALS
Volume: 37
Issue: 7
起始頁: 962
結束頁: 967
顯示於類別:期刊論文


文件中的檔案:

  1. 000255876300005.pdf

若為 zip 檔案,請下載檔案解壓縮後,用瀏覽器開啟資料夾中的 index.html 瀏覽全文。