標題: Twisted Nematic Liquid-Crystal-Based Terahertz Phase Shifter using Pristine PEDOT: PSS Transparent Conducting Electrodes
作者: Sahoo, Anup Kumar
Yang, Chan-Shan
Yen, Chun-Ling
Lin, Hung-Chun
Wang, Yu-Jen
Lin, Yi-Hsin
Wada, Osamu
Pan, Ci-Ling
光電工程學系
Department of Photonics
關鍵字: liquid crystals;LC;twisted nematic;TN;phase shifter;PEDOT: PSS;transparent conducting electrode;TCE;terahertz;THz
公開日期: 2-Feb-2019
摘要: For this study, we demonstrated three different types of twisted nematic (TN) liquid crystal (LC) terahertz (THz) phase shifters using pristine poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT: PSS) thin films as transparent conducting electrodes (TCEs). The transmittance of spin-coated pristine PEDOT: PSS thin film was as high as 92% in the frequency range of 0.2-1.2 THz. This is among the highest reported. Several TN-LC cells were constructed in a comparative study, which confirmed the reliability of pristine PEDOT: PSS as a TCE layer for THz phase shifter applications. The highest phase shift, required root-mean-square (RMS) driving voltage, and threshold voltage achieved by devices tested were 95.2 degrees at 1 THz, 7.2 V-RMS, and 0.5 V-RMS, respectively. The thickness of the LC layer for the phase shifter was 250 mu m, approximately half as thick as previous designs. In addition, the pristine PEDOT: PSS-based TN-LC phase shifter exhibited a figure-of-merit (FOM) value of approximately 6.65 degree.dB(-1).V-1. This compared favorably with previously reported homogeneously aligned phase shifters with an FOM of 2.19 degree.dB(-1).V-1. Our results indicated that a twisted nematic LC cell with pristine PEDOT: PSS thin films as electrodes is a good combination for a THz phase shifter and wave plates as well as other LC-based THz devices.
URI: http://dx.doi.org/10.3390/app9040761
http://hdl.handle.net/11536/148977
ISSN: 2076-3417
DOI: 10.3390/app9040761
期刊: APPLIED SCIENCES-BASEL
Volume: 9
Appears in Collections:Articles


Files in This Item:

  1. 0f96c8f7c0e03e197930cd85b3befd3b.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.