Ni silicide formation on epitaxial Si1-yCy/(001) layers

Abstract

The formation of Ni silicides on Si1 - yCy (y=0.01 and 0.018) epilayers grown on Si(001) has been investigated. The presence of C atoms was found to significantly retard the growth kinetics of NiSi and enhances the thermal stability of thin NiSi films. For Ni(11 nm)/Si0.982C0.018 samples, the process window of NiSi was shifted and extended to 450-700 degrees C. Moreover, there was an additional strain introduced into the Si1 - yCy epilayers during Ni silicidation. This work shows the potential of Ni silicidation on Si1yCy for device applications. (C) 2010 Elsevier B.V. All rights reserved.