標題: Relationships between the crystalline phase of an IGZO target and electrical properties of a-IGZO channel film
作者: Lee, Yih-Shing
Dai, Zuo-Ming
Lin, Cheng-I
Lin, Horng-Chih
電子工程學系及電子研究所
Department of Electronics Engineering and Institute of Electronics
關鍵字: Films;X-ray methods;Electrical properties;IGZO
公開日期: 1-Jan-2012
摘要: This study used powders containing different In2O3-Ga2O3-ZnO (IGZO) chemical compositions to manufacture targets using a metallurgical process. The resulting targets were used to deposit amorphous In-Ga-Zn-O (a-IGZO) channel films by a radio frequency magnetron sputtering process. This study examined the relationships between these target compositions and crystalline phases of the powders and the resulting material characterization, examining the impacts on electrical characteristics of a-IGZO films with varied O-2 flow rates. The ternary compound phase of ZnGa2O4 became stable at 1000 degrees C according to XRD diagrams at different calcining temperatures. An analysis of the XRD diagrams of different compositions of IGZO powders showed that the atomic ratio of ZnO is larger than that of In2O3 and Ga2O3, and that the main peaks (1 0 1) and (0 0 15) intensity of the respective InGaZnO4 and lnGaZnO6 phases intensity would increase. Ceramic targets with different compositions were used to deposit the a-IGZO films with varied O-2 flow rates. When the O-2 flow rate was zero, the results of a Hall measurement of a-IGZO films deposited from targets with higher Zn atomic ratio showed lower resistivity, higher carrier concentration, and lower mobility. Nevertheless, as the O-2 flow rate was more than 5 sccm, increasing the atom ratio of Zn in the IGZO ceramic target obviously increased the capability of capturing O-2 in the a-IGZO films, leading to higher resistivity, lower carrier concentration (<10(18) cm(-3)), and higher mobility. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
URI: http://dx.doi.org/10.1016/j.ceramint.2011.05.105
http://hdl.handle.net/11536/15085
ISSN: 0272-8842
DOI: 10.1016/j.ceramint.2011.05.105
期刊: CERAMICS INTERNATIONAL
Volume: 38
Issue: 
起始頁: S595
結束頁: S599
Appears in Collections:Conferences Paper


Files in This Item:

  1. 000299589800133.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.