標題: Deep-ultraviolet Schottky photodetectors with high deep-ultraviolet/visible rejection based on a ZnGa2O4 thin film
作者: Tsai, Si-Han
Shen, Yuan-Chu
Huang, Chiung-Yi
Horng, Ray-Hua
電子工程學系及電子研究所
Department of Electronics Engineering and Institute of Electronics
關鍵字: Single-crystalline ZnGa2O4 epilayer;Sapphire;Schottky deep-ultraviolet photodetector
公開日期: 1-Dec-2019
摘要: A single-crystalline ZnGa2O4 epilayer was successfully grown on a c-plane (0001) sapphire substrate through metalorganic chemical vapor deposition. A metal-semiconductor-metal Schottky deep-ultraviolet (DUV) photodetector based on a ZnGa2O4 thin film was fabricated through a simple process of E-gun evaporation and thermal annealing. At a bias of 10 V, the ZnGa2O4 photodetectors exhibited excellent performance characteristics such as an extremely low dark current (0.86 pA), a responsivity of 0.46 A/W under 230-nm DUV, a high photo/dark current ratio (up to 4.68x10(4)), a sharp cutoff wavelength of approximately 270 nm, and short rise and fall times of 0.96 and 0.34 s. The photogenerated holes trapped in the Schottky barrier and the shrinking of the depletion region under DUV illumination enabled high DUV/visible rejection ratio (3-4 orders with a 20-V bias). Therefore, the Fowler-Nordheim field tunneling emission functioned as the main electron transport mechanism under DUV illumination and improved the photoelectric characteristics of the epilayer.
URI: http://dx.doi.org/10.1016/j.apsusc.2019.143670
http://hdl.handle.net/11536/153110
ISSN: 0169-4332
DOI: 10.1016/j.apsusc.2019.143670
期刊: APPLIED SURFACE SCIENCE