標題: Failure induced by thermomigration of interstitial Cu in Pb-free flip chip solder joints
作者: Chen, Hsiao-Yun
Chen, Chih
Tu, King-Ning
材料科學與工程學系
Department of Materials Science and Engineering
公開日期: 22-Sep-2008
摘要: Failure induced by thermomigration in Pb-free SnAg flip chip solder joints has been investigated by electromigration tests under 9.7 x 10(3) A/cm(2) at 150 degrees C. The fast interstitial diffusion of Cu atoms from underbump metallization into Sn matrix caused void formation at the passivation opening on the chip side. The Cu diffusion was driven by a large thermal gradient and led to void formation even in the neighboring unpowered bumps. When the thermal gradient is above 400 degrees C/cm, theoretical calculation indicates that the thermomigration force is greater than the electromigration force at 9.7 x 10(3) A/cm(2) stressing. (C) 2008 American Institute of Physics.
URI: http://dx.doi.org/10.1063/1.2990047
http://hdl.handle.net/11536/8343
ISSN: 0003-6951
DOI: 10.1063/1.2990047
期刊: APPLIED PHYSICS LETTERS
Volume: 93
Issue: 12
結束頁: 
Appears in Collections:Articles


Files in This Item:

  1. 000259799100034.pdf

If it is a zip file, please download the file and unzip it, then open index.html in a browser to view the full text content.